Skripsi teknik mesin dengan judul ” PENGARUH FRAKSI VOLUME SERAT TERHADAP KUAT TARIK DAN TEKAN MATERIAL KOMPOSIT UNIDIREKSIONAL SERAT IJUK AREN/POLYESTER c” berikut bisa Kamu unduh disini, dan masih banyak skripsi terupdate lainnya.

Summary

The utilization of sugar palm fibers is restricted to the manufacture of brooms, ropes and industrial constructing filtration supplies and water absorption.The usefulness is just not separated from the properties of fibers that elastic, arduous, very immune to acidic water and salt-containing water, and troublesome to digest by harmful organisms.To date, this sort of palm fibers is barely used on the whole and has not been used particularly by using the potential traits of mechanical properties in holding the burden of Pull and press as materials for the construction.
The fabric used on this analysis sugar palm fibers with polyester matrix and processed by utilizing press mildew technique approach. The check specimens had been ready in line with ASTM D638 requirements for tensile specimens and ASTM 3410 for compressive specimens. Variations in fiber quantity fraction had been planed being zero%, 10%, 20%, 30%, and 40% for tensile and press specimens
The precise fiber quantity fraction after being analyzed for being zero%; 10,54%; 19,42%; 27,74%; and 40,83 % for tensile specimen had been discovered. Whereas for compressive specimens ware discovered being zero%; 10,98%; 16, 56 %; 28,89 %; and 39,36% . Testing outcomes present that the larger the fiber quantity fraction will increase the tensile power however decreases the worth of compressive power. The highnest, tensile power was discovered at Vf 40,83 % which is 43,259 MPa and the smallest tensile power is at Vf zero% which is 33,437 MPa, and for the highnest compressive power was discovered at zero,zero% Vf which is 87,253 MPa and the bottom compression power was discovered at Vf 16,56 % which is 50,464 MPa. For the highnest tensile modulus was discovered at Vf 40,83 % which is 1754,65 MPa and the lownest tensile elastic modulus was discovered at Vf zero% which is 1380,13 MPa,

Inilah skripsi terkait ” PENGARUH FRAKSI VOLUME SERAT TERHADAP KUAT TARIK DAN TEKAN MATERIAL KOMPOSIT UNIDIREKSIONAL SERAT IJUK AREN/POLYESTER ” ini. perlu anda tahu skripsi ini asalnya dari situs luar

Silahkan ke URL berikut untuk melakukan unduh

DOWNLOAD

Tinggalkan Balasan

Alamat email Anda tidak akan dipublikasikan. Ruas yang wajib ditandai *