download tesis FISIKA lengkap
download tesis FISIKA lengkap

Tesis fisika dengan judul ” Pemanfaatan Limbah LDPE dan serat pendek sabut kelapa dengan gabungan aspal dan pasir dalam pembuatan genteng komposit polimer c” ini dapat Kamu download disini, dan masih banyak skripsi terupdate lainnya.

Sudah dilakukan riset tentang pemanfaatan limbah LDPE (Low Density Poly Ethilen) dan serat pendek sabut kelapa dengan gabungan aspal dan pasir dalam pembuatan genteng komposit polimer. Riset ini dimaksudkan untuk mengetahui pengaruh variasi komposisi serat pendek sabut kelapa dan pengurangan pasir terhadap karakteristik genteng. Sampel dibikin dengan komposisi LDPE, aspal yang dipakai tetap, yaitu 30%, 5% dari massa complete sampel, sedangkan persentase komposisi pasir dan serat pendek sabut kelapa divariasikan dengan perbandingan; (65:zero), (64:1), (63: 2), (62:three), (61:four) dan (60:5). Karakterisasi yang dilakukan mencakup pengujian kerapatan, daya serap air, uji tarik, uji lentur, uji impak, uji waktu nyala dan jarak bakar dan uji DTA. Hasil riset menjelaskan bahwa karakteristik genteng sangat dipengaruhi oleh komposisi serat. Karakteristik maksimal didapatkan pada komposisi (30:5:60:5) dengan nilai kerapatan 1239 kg/m3 mendekati nilai genteng komersil yaitu 1500 kg/m3, daya serap air zero,1% lebih kecil dari daya serap air genteng komersil sebesar zero,6%, kekuatan tarik 1,99 MPa, kekuatan lentur eight,96 MPa mendekati nilai kuat lentur genteng komersil sebesar 10 MPa, kekuatan impak 24 kJ/m2, waktu penyalaan spesimen ialah 622,33 detik dan jarak bakar spesimen zero.09 m. Nilai puncak endoterm dan eksoterm masing-masing yaitu 120 0C dan 480 0C. Penambahan serat pendek sabut kelapa bisa menurunkan sifat fisisnya tetapi bisa meningkatkan sifat mekanik dan termalnya.

 

The analysis on the utilization of waste LDPE (Low Density Poly Ethilen) and quick fibers with a mix of coconut fiber and sand bitumen within the manufacture of polymer composite tile has been performed. This research aimed to find out the impact of variations within the composition of quick coir fiber and discount of sand on the traits of tile. Samples made with the composition of LDPE, used asphalt stays, specifically 30%, 5% of the entire mass of the pattern, whereas the share composition of sand and coconut coir fiber diversified quick by comparability; (65:zero), (64:1), (63: 2), (62:three), (61:four) and (60:5). Characterization testing was performed on the density, water absorption, tensile take a look at, bending take a look at, impression take a look at, flame take a look at of time and distance take a look at gasoline and DTA. The outcomes confirmed that the traits of the tile is strongly influenced by the composition of the fibers. Most traits obtained on the composition (30:5:60:5) with density 1239 kg/m3 worth approaching industrial tile worth is 1500 kg/m3, water absorption is lower than zero.1% water absorption of zero.6% industrial tile, 1.99 MPa tensile power, flexural power of eight.96 MPa flexural power values approaching industrial tile at 10 MPa, impression power 24 kJ/m2, time is 622,33 seconds specimen ignition and gasoline specimen zero,09 m distance. Endothermic and exothermic peak values respectively of 120 0C and 480 0C. The addition of quick coir fiber can decrease his bodily properties, however can enhance the mechanical and thermal properties.

 

Inilah skripsi mengenai ” Pemanfaatan Limbah LDPE dan serat pendek sabut kelapa dengan gabungan aspal dan pasir dalam pembuatan genteng komposit polimer ” ini. perlu anda ketahui skripsi ini berasal dari situs luar

Silahkan ke hyperlink berikut untuk melakukan unduh

DOWNLOAD

Tinggalkan Balasan

Alamat email Anda tidak akan dipublikasikan. Ruas yang wajib ditandai *